TASK™ 2

Task2x ⓘ B80DD09C-DD3A-1C45-90A9-1A6D68097AA0
Polyurethane Resin
exclamation.svg health-hazard.svg

Danger

H315 - Verursacht Hautreizungen.
H317 - Kann allergische Hautreaktionen verursachen.
H320 - Verursacht Augenreizung.
H332 - Gesundheitsschädlich bei Einatmen.
H334 - Kann bei Einatmen Allergie, asthmaartige Symptome oder Atembeschwerden verursachen.
€ 168,23

(€ 141,37 ohne 19% MwSt.)

Auf Lager

Beschreibung

Materials should be stored and used in a warm environment 23°C. These products have a limited shelf life and should be used as soon as possible. All liquid urethanes are moisture sensitive and will absorb atmospheric moisture. Mixing tools and containers should be clean and made of metal, glass or plastic. Mixing should be done in a well-ventilated area. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk.Because no two applications are quite the same, a small test application to determine suitability is recommended if performance of this material is in question.Applying A Release Agent - If you are unsure about surface compatibility, a trial casting on a surface finish similar to the final mold or model should be made to avoid damage to the working surface. Polyurethane, latex or metal molds should be dry and require a coat of suitable release agent. Universal Mold Release (available from Form X) is ideal for this purpose. A liberal coat of release agent should be applied onto all surfaces that will contact the plastic. To ensure thorough coverage, lightly brush the release agent with a soft brush over all surfaces. Follow with a light mist coating and let the release agent dry for 30 minutes.IMPORTANT: Shelf life of product is reduced after opening. Remaining product should be used as soon as possible. Immediately replacing the lids on both containers after dispensing product will help prolong the shelf life of the unused product. XTEND-IT™ Dry Gas Blanket (available from Smooth-On) will significantly prolong the shelf life of unused liquid urethane products.Measuring - The proper mixing ratio is 1A:1B by volume or 115A:100B by weight. Dispense the required amount of Part A into a mixing container. Dispense the appropriate amount of Part B and combine with Part A.Mixing - Materials should be stored and used in a warm environment 23° C. Shake Part A & Part B before using. Add Part A to Part B and mix thoroughly. Stir slowly and deliberately making sure that you scrape the sides and bottom of the mixing container several times. Be careful not to splash low viscosity material out of container. Remember, product sets up quickly. The higher the mass concentration, the faster the material gels and cures. Do not delay between mixing and pouring.Vacuuming - TASK™ products are low in viscosity and do not require vacuum degassing. If you choose to vacuum the material, subject mixture to 29 h.i.g. mercury in a vacuum chamber until mixture rises, breaks and falls. Allow for 3 to 4 times volume expansion in mixing container. Be aware of pot life so that material does not set up in mixing container.Pouring - Pour mixture in a single spot at the lowest point of the mold. Let the mixture seek its level. A uniform flow will help minimize entrapped air.For Best Results . . . Best results are obtained using a pressure casting technique. After pouring the mixed compound, the entire casting assembly (mold, dam structure, etc.) is placed in a pressure chamber and subjected to 60 PSI (4.2 kg/cm2) air pressure for the full cure time of the material.Curing - Important: Use this product with at least room size ventilation or in proximity to a forced outlet air vent and do not inhale/breath fumes. Fumes, which may be visible with a significant mass concentration, will quickly dissipate with adequate ventilation. Castings with significant mass may be hot to the touch and irritate skin immediately following cure. Let casting cool to room temperature before handling.Demold time of the finished casting depends on mass and mold configuration. Low mass or thin-walled castings will take longer to cure than castings with higher mass concentration.If making rotational or hollow castings, backfilling with a rigid foam (Foam-iT! 5 or other) will provide lightweight reinforcement. Foam backfilling is recommended if castings will be subjected to temperatures above 30°C.Post Curing - Castings will reach “full cure” faster and achieve maximum physical properties and heat resistance if TASK™ 2 is post cured. Castings should be post cured in a mold or support structure. Allow the material to cure for full cure time at room temperature followed by 4 - 8 hours at 65 - 72°C. The casting or part should be allowed to cool to room temperature before handling.Warning: Fumes, which may be visible as this product starts to “gel” and cure, will dissipate with adequate ventilation. Only use this product with room size ventilation and do not inhale/breathe fumes. Castings will be extremely hot immediately following cure and may burn the skin. Let cool to room temperature before handling.Performance - Cured castings are rigid and durable. They resist moisture, moderate heat, solvents, dilute acids and can be machined, primed/painted or bonded to other surfaces (any release agent must be removed). If machining cured TASK™ plastics, wear dust mask or other apparatus to prevent inhalation of residual particles. Castings can be displayed outdoors after priming and painting.

Anleitung

Spezifikationen

Color White
Mixed Viscocity 150 cps
Cure Time 60 minutes
Pot Life 7 minutes
Flexural Strength 9,500 psi
Flexural Modulus 288,000 psi
Specific Volume 24.7 cu. in./lb.
Specific Gravity 1.12 g/cc
Mix Ratio By Weight 115A:100B
Shrinkage 0.005 in. / in.
Mix Ratio By Volume 1A:1B
Tensile Strength 6,650 psi
Elongation At Break 6 %
Shore D Hardness 80
Heat Deflection Temp 134 °F
Compressive Strength 8,300 psi
Tensile Modulus 290,000 psi
Compressive Modulus 78,000 psi
Verfügbar in Polyurethane Resin
Product Cure Time Specific Gravity Specific Volume Tensile Strength Tensile Modulus Compressive Strength Compressive Modulus Flexural Strength Shrinkage Heat Deflection Temp Elongation At Break Flexural Modulus Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Shore D Hardness Color Mixed Viscocity Cure Time Pot Life Flexural Strength Flexural Modulus Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore D Hardness Heat Deflection Temp Compressive Strength Tensile Modulus Compressive Modulus Handling Time Handling Time Heat Deflection With Post Cure Heat Deflection With Post Cure Shore A Hardness Die C Tear Strength Hundred Percent Modulus Hundred Percent Modulus Die C Tear Strength Shore A Hardness
TASK™ 2 60 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.005 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 7 min. 80 White 150 cps 60 min. 7 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.005 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 3 90 min. 1.12 g/cc 24.7 cu. in./lb. 6,650 psi 290,000 psi 8,300 psi 78,000 psi 9,500 psi 0.0025 in. / in. 134 °F 6 % 288,000 psi 150 cps 1A:1B 115A:100B 20 min. 80 White 150 cps 90 min. 20 min. 9,500 psi 288,000 psi 24.7 cu. in./lb. 1.12 g/cc 115A:100B 0.0025 in. / in. 1A:1B 6,650 psi 6 % 80 134 °F 8,300 psi 290,000 psi 78,000 psi - - - - - - - - - -
TASK™ 4 16 h. 1.167 g/cc 23.9 cu. in./lb. 6,500 psi 130,000 psi 7,400 psi 75,000 psi 9,000 psi 0.0035 in. / in. 110 °F 4 % 204,000 psi 250 cps - 100A:100B 20 min. 83 Ivory 250 cps 16 h. 20 min. 9,000 psi 204,000 psi 23.9 cu. in./lb. 1.167 g/cc 100A:100B 0.0035 in. / in. - 6,500 psi 4 % 83 110 °F 7,400 psi 130,000 psi 75,000 psi - - - - - - - - - -
TASK™ 5 24 h. 1.1 g/cc 25.2 cu. in./lb. 4,530 psi 200,000 psi 6,700 psi 83,000 psi 6,480 psi 0.007 in. / in. 145 °F 5 % 216,000 psi 600 cps 1A:1B 1A:1B 3 min. 77 Tan 600 cps 24 h. 3 min. 6,480 psi 216,000 psi 25.2 cu. in./lb. 1.1 g/cc 1A:1B 0.007 in. / in. 1A:1B 4,530 psi 5 % 77 145 °F 6,700 psi 200,000 psi 83,000 psi 15 min. 15 min. - - - - - - - -
TASK™ 6 24 h. 1.07 g/cc 25.9 cu. in./lb. 5,200 psi 146,000 psi 5,570 psi 65,000 psi 6,200 psi 0.0031 in. / in. 162 °F 4 % 182,500 psi 800 cps 1A:1B 1A:1B 7 min. 75 Tan 800 cps 24 h. 7 min. 6,200 psi 182,500 psi 25.9 cu. in./lb. 1.07 g/cc 1A:1B 0.0031 in. / in. 1A:1B 5,200 psi 4 % 75 162 °F 5,570 psi 146,000 psi 65,000 psi 75 min. 75 min. - - - - - - - -
TASK™ 7 10 min. 1.2 g/cc 23.1 cu. in./lb. 3,390 psi 150,700 psi 5,140 psi 57,600 psi 5,450 psi 0.0111 in. / in. 131 °F 15.1 % 148,900 psi 200 cps 1A:1B 104A:100B 2.5 min. 73 Off-White 200 cps 10 min. 2.5 min. 5,450 psi 148,900 psi 23.1 cu. in./lb. 1.2 g/cc 104A:100B 0.0111 in. / in. 1A:1B 3,390 psi 15.1 % 73 131 °F 5,140 psi 150,700 psi 57,600 psi - - - - - - - - - -
TASK™ 8 15 min. 1.09 g/cc 25.4 cu. in./lb. 5,840 psi 246,000 psi 8,760 psi 77,400 psi 8,280 psi 0.01 in. / in. 194 °F 4 % 271,000 psi 100 cps 1A:1B 120A:100B 2.5 min. 80 Off-White 100 cps 15 min. 2.5 min. 8,280 psi 271,000 psi 25.4 cu. in./lb. 1.09 g/cc 120A:100B 0.01 in. / in. 1A:1B 5,840 psi 4 % 80 194 °F 8,760 psi 246,000 psi 77,400 psi - - 263 °F 263 °F - - - - - -
TASK™ 11 16 h. 1.12 g/cc 24.7 cu. in./lb. 2,500 psi - - - - 0.0024 in. / in. - 100 % - 2,000 cps - 100A:100B 20 min. 60 Translucent White 2,000 cps 16 h. 20 min. - - 24.7 cu. in./lb. 1.12 g/cc 100A:100B 0.0024 in. / in. - 2,500 psi 100 % 60 - - - - - - - - - - - - - -
TASK™ 12 16 h. 1.08 g/cc 26 cu. in./lb. 2,700 psi - - - - 0.001 in. / in. - 300 % - 2,400 cps - 100A:44B 20 min. 60 Clear Amber 2,400 cps 16 h. 20 min. - - 26 cu. in./lb. 1.08 g/cc 100A:44B 0.001 in. / in. - 2,700 psi 300 % 60 - - - - - - - - - - - - - -
TASK™ 13 20 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.005 in. / in. - 125 % - 800 cps - 100A:120B 3 min. 50 Black 800 cps 20 min. 3 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.005 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 14 45 min. 1.15 g/cc 24.1 cu. in./lb. 1,800 psi - - - - 0.0035 in. / in. - 125 % - 800 cps - 100A:120B 10 min. 50 Black 800 cps 45 min. 10 min. - - 24.1 cu. in./lb. 1.15 g/cc 100A:120B 0.0035 in. / in. - 1,800 psi 125 % 50 - - - - - - - - - - - - - -
TASK™ 15 1 h. 1.12 g/cc 24.7 cu. in./lb. 2,720 psi 126,000 psi 5,450 psi 60,000 psi 5,450 psi 0.0042 in. / in. 117 °F 20 % 170,000 psi 600 cps - 75A:100B 6 min. 75 Opaque White 600 cps 1 h. 6 min. 5,450 psi 170,000 psi 24.7 cu. in./lb. 1.12 g/cc 75A:100B 0.0042 in. / in. - 2,720 psi 20 % 75 117 °F 5,450 psi 126,000 psi 60,000 psi - - - - - - - - - -
TASK™ 16 24 h. 1.08 g/cc 25.64 cu. in./lb. 2,264 psi - - - - 0.0025 in. / in. - 233 % - 1,400 cps - 1A:2B 6 min. 30 Light Yellow 1,400 cps 24 h. 6 min. - - 25.64 cu. in./lb. 1.08 g/cc 1A:2B 0.0025 in. / in. - 2,264 psi 233 % 30 - - - - 90 min. 90 min. - - 80 197 pli 855 psi 855 psi 197 pli 80
TASK™ 18 16 h. 1.57 g/cc 17.6 cu. in./lb. 3,250 psi 514,000 psi 8,420 psi 97,300 psi 10,700 psi 0.0006 in. / in. 149 °F 1 % 86,000 psi 4,400 cps - 26A:100B 20 min. 88 Metal Gray 4,400 cps 16 h. 20 min. 10,700 psi 86,000 psi 17.6 cu. in./lb. 1.57 g/cc 26A:100B 0.0006 in. / in. - 3,250 psi 1 % 88 149 °F 8,420 psi 514,000 psi 97,300 psi - - - - - - - - - -
TASK™ 21 1 h. 1.07 g/cc 25.9 cu. in./lb. 5,500 psi 270,000 psi 7,100 psi 78,500 psi 7,100 psi 0.0058 in. / in. 144 °F 7.5 % 250,000 psi 500 cps 2A:1B 2A:1B 6 min. 75 White 500 cps 1 h. 6 min. 7,100 psi 250,000 psi 25.9 cu. in./lb. 1.07 g/cc 2A:1B 0.0058 in. / in. 2A:1B 5,500 psi 7.5 % 75 144 °F 7,100 psi 270,000 psi 78,500 psi - - - - - - - - - -

Warum bei FormX kaufen?

Abonnieren Sie unseren Newsletter

Erhalten Sie 5,- € Rabatt auf Ihren ersten Einkauf!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Diese Website wurde entwickelt von Usecue B.V.
© 2026 FormX B.V.