OOMOO™ 25

OOMOO25pint ⓘ AE2D8D6F-106C-B649-80E5-D7BB54CD2DF1
Tin Cure Silicone
€ 39,97

(€ 33,59 ohne 19% MwSt.)

Auf Lager

Beschreibung

Zinn katalysierter Siliconkautschuk. Leicht zu mischen. Shore Härte 25A.

Anleitung

Spezifikationen

Hundred Percent Modulus 100 psi
Color Light Blue
Die B Tear Strength 40 pli
Mixed Viscocity 4,250 cps
Useful Temperature Min -65 °F
Cure Time 75 minutes
Pot Life 15 minutes
Specific Volume 20.6 cu. in./lb.
Specific Gravity 1.34 g/cc
Mix Ratio By Weight 100A:130B
Shrinkage 0.0025 in. / in.
Mix Ratio By Volume 1A:1B
Tensile Strength 240 psi
Elongation At Break 250 %
Shore A Hardness 25
Verfügbar in Tin Cure Silicone
Product Cure Time Shore A Hardness Specific Gravity Specific Volume Tensile Strength Shrinkage Elongation At Break Hundred Percent Modulus Die B Tear Strength Useful Temperature Min Mixed Viscocity Mix Ratio By Volume Mix Ratio By Weight Pot Life Hundred Percent Modulus Color Die B Tear Strength Mixed Viscocity Useful Temperature Min Cure Time Pot Life Specific Volume Specific Gravity Mix Ratio By Weight Shrinkage Mix Ratio By Volume Tensile Strength Elongation At Break Shore A Hardness
OOMOO™ 30 6 h. 30 1.34 g/cc 20.6 cu. in./lb. 240 psi 0.0025 in. / in. 250 % 100 psi 40 pli -65 °F 4,250 cps 1A:1B 100A:130B 30 min. 100 psi Lavender 40 pli 4,250 cps -65 °F 6 h. 30 min. 20.6 cu. in./lb. 1.34 g/cc 100A:130B 0.0025 in. / in. 1A:1B 240 psi 250 % 30
OOMOO™ 25 75 min. 25 1.34 g/cc 20.6 cu. in./lb. 240 psi 0.0025 in. / in. 250 % 100 psi 40 pli -65 °F 4,250 cps 1A:1B 100A:130B 15 min. 100 psi Light Blue 40 pli 4,250 cps -65 °F 75 min. 15 min. 20.6 cu. in./lb. 1.34 g/cc 100A:130B 0.0025 in. / in. 1A:1B 240 psi 250 % 25

Warum bei FormX kaufen?

Abonnieren Sie unseren Newsletter

Erhalten Sie 5,- € Rabatt auf Ihren ersten Einkauf!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Diese Website wurde entwickelt von Usecue B.V.
© 2026 FormX B.V.