Holden's Mold Making Latex High Viscosity HX-974™

HX974BrushWhiQt ⓘ 1584190D-256C-7E46-B43E-BF14D24F36A1
Latex
exclamation.svg health-hazard.svg

Danger

H315 - Verursacht Hautreizungen.
H317 - Kann allergische Hautreaktionen verursachen.
H319 - Verursacht schwere Augenreizung.
H334 - Kann bei Einatmen Allergie, asthmaartige Symptome oder Atembeschwerden verursachen.
€ 28,41

(€ 23,87 ohne 19% MwSt.)

Auf Lager

Beschreibung

HX-974™ White Brushable Mold Making Latex is a vulcanizable, high viscosity latex made especially for vertical surface applications. With a higher viscosity than HX-80, this product is ideal for making glove molds of 3-dimensional originals and statuary. Brush on between 10 and 20 layers (depending on model) and let rubber cure to a highly elastic, wear resistant mold that captures perfect detail. Molds are suitable for casting plaster, concrete and wax. Applications for HX-974™ White Latex include making molds for making ornamental concrete castings, stone veneer, architectural gypsum ornament and wax castings like candles. NOTE: Latex can be used for limited casting of some resins. The higher the exotherm of the casting material, the quicker the mold will degrade and become unusable.Mold MaxTM silicone rubbers would be a better choice for production casting of resins.Allergies: Read label carefully. Do not use this product if you have known allergies to rubber latex. If you're unsure, bring the label to your doctor for their advice. If an allergic reaction occurs, stop use and seek medical help right away.

Anleitung

Spezifikationen

Color White
Full Cure Time 7 days at 23°C
Storage Temperature < 49°C
Specific Gravity 0.95
Shrinkage 5-10%
Viscosity 7,000-9,000 cps
Solids Content 56-60%
Copper Content < 8 ppm
Manganese Content < 8 ppm
Potassium Hydroxide (KOH) 0.800000
Mechanical Stability 650 seconds
Accelerated Cure Time 8-12 hours at 43-49°C
Minimum Layers For Thickness 10 layers
Thickness For Smaller Items 0.16 cm
Thickness For Larger Items 0.32 cm
Verfügbar in Latex
Product Color Storage Temperature Cure Time Viscosity Shelf Life Operating Temperature Minimum Layers For Thickness Thickness For Smaller Items Thickness For Larger Items Full Cure Temperature Range Full Cure Time At Elevated Temperature Full Cure Time Specific Gravity Shrinkage Solids Content Copper Content Manganese Content Potassium Hydroxide (KOH) Mechanical Stability Accelerated Cure Time
Holden's Mold Making Latex HX-80™ Natural Below 49°C 7 days at 23°C Low Limited 23°C 10 layers 0.16 cm 0.32 cm 43°C to 49°C 8-12 h. - - - - - - - - -
Holden's Mold Making Latex High Viscosity HX-974™ White < 49°C - 7,000-9,000 cps - - 10 layers 0.16 cm 0.32 cm - - 7 days at 23°C 0.95 5-10% 56-60% < 8 ppm < 8 ppm 0.800000 650 sec. 8-12 h. at 43-49°C
Holden's Coating/Dipping Latex - - - - Limited 23°C - - - - - - - - - - - - - -
Holden's Frisket Mask Latex - - - - - 23°C - - - - - - - - - - - - - -

Warum bei FormX kaufen?

Abonnieren Sie unseren Newsletter

Erhalten Sie 5,- € Rabatt auf Ihren ersten Einkauf!

Visa logo iDeal logo Mastercard logo Paypal logo FedEx logo FedEx logo
Diese Website wurde entwickelt von Usecue B.V.
© 2026 FormX B.V.