Ein thixotropes Epoxid-Gelcoat, das häufig für Handlaminier- und Werkzeuganwendungen verwendet wird, "farbneutral" speziell zum Hinzufügen von Farbpigmenten und Füllstoffen.
Thixotropes Epoxid-Gelcoat mit hoher Abriebfestigkeit.
Thixotropes Epoxidgelcoat für Laminier- und Werkzeuganwendungen.
Thixotropes Epoxid-Gelcoat für Handlaminier- und Werkzeuganwendungen.
| Product | Cure Time | Barcol 935 Hardness | Specific Gravity | Specific Volume | Color | Compressive Strength | Flexural Strength | Shrinkage | Heat Deflection Temp | Ultimate Tensile | Thin Film Working Time | Thin Film Recoat Time | Tack Free Time | Mixed Viscocity | Mix Ratio By Volume | Mix Ratio By Weight | Pot Life | Shore D Hardness | Color | Mixed Viscocity | Cure Time | Flexural Strength | Pot Life | Specific Volume | Specific Gravity | Mix Ratio By Weight | Shrinkage | Mix Ratio By Volume | Tack Free Time | Ultimate Tensile | Shore D Hardness | Heat Deflection Temp | Thin Film Working Time | Compressive Strength | Thin Film Recoat Time | Barcol 935 Hardness |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| EpoxAcoat™ NEUTRAL | 16 h. | 87 | 1.43 g/cc | 19.4 cu. in./lb. | Neutral | 24,000 psi | 30,000 psi | 0.00015 in. / in. | 133 °F | 26,000 psi | 40 min. | 60 min. | 4 h. | Light Paste | 5A:1B | 100A:15B | 20 min. | 85 | Neutral | Light Paste | 16 h. | 30,000 psi | 20 min. | 19.4 cu. in./lb. | 1.43 g/cc | 100A:15B | 0.00015 in. / in. | 5A:1B | 4 h. | 26,000 psi | 85 | 133 °F | 40 min. | 24,000 psi | 60 min. | 87.000000 |
| EpoxAcoat™ GREY | 16 h. | 87 | 1.43 g/cc | 19.4 cu. in./lb. | Grey | 24,000 psi | 30,000 psi | 0.00015 in. / in. | 133 °F | 26,000 psi | 40 min. | 60 min. | 4 h. | Light Paste | 5A:1B | 100A:15B | 20 min. | 85 | Grey | Light Paste | 16 h. | 30,000 psi | 20 min. | 19.4 cu. in./lb. | 1.43 g/cc | 100A:15B | 0.00015 in. / in. | 5A:1B | 4 h. | 26,000 psi | 85 | 133 °F | 40 min. | 24,000 psi | 60 min. | 87.000000 |
| EpoxAcoat™ WHITE | 16 h. | 87 | 1.43 g/cc | 19.4 cu. in./lb. | White | 24,000 psi | 30,000 psi | 0.00015 in. / in. | 133 °F | 26,000 psi | 40 min. | 60 min. | 4 h. | Light Paste | 5A:1B | 100A:15B | 20 min. | 85 | White | Light Paste | 16 h. | 30,000 psi | 20 min. | 19.4 cu. in./lb. | 1.43 g/cc | 100A:15B | 0.00015 in. / in. | 5A:1B | 4 h. | 26,000 psi | 85 | 133 °F | 40 min. | 24,000 psi | 60 min. | 87.000000 |
| EpoxAcoat™ RED | 16 h. | 87 | 1.43 g/cc | 19.4 cu. in./lb. | Red | 24,000 psi | 30,000 psi | 0.00015 in. / in. | 133 °F | 26,000 psi | 40 min. | 60 min. | 4 h. | Light Paste | 5A:1B | 100A:15B | 20 min. | 85 | Red | Light Paste | 16 h. | 30,000 psi | 20 min. | 19.4 cu. in./lb. | 1.43 g/cc | 100A:15B | 0.00015 in. / in. | 5A:1B | 4 h. | 26,000 psi | 85 | 133 °F | 40 min. | 24,000 psi | 60 min. | 87.000000 |
Seit über dreißig Jahren suchen wir weltweit nach den hochwertigsten Materialien für Modellbau, Formenbau und Guss.
Von Silikonen und Harzen bis zu Jesmonite und Special-Effects-Materialien — ein sorgfältig kuratiertes Sortiment für Profis, Künstler und Macher.
Unser Vertriebsteam ist bekannt für sein Wissen und Engagement und unterstützt Sie bei Formenbau, Guss, Bildhauerei und Prototyping.
Wir versenden aus unseren Lagern in Amsterdam, Barcelona und Madrid an Kunden in ganz Europa, von Griechenland bis Norwegen.
FormX wurde in Amsterdam gegründet und wuchs von einer lokalen Kunstgießerei zu einem bedeutenden europäischen Lieferanten — mit festen Wurzeln in der Stadt.
FormX ist auf die Versorgung und den spezialisierten Handel mit 3D-Modelliermaterialien im weitesten Sinne des Wortes spezialisiert und verfügt über Lager und Showrooms in Amsterdam, Barcelona und Madrid.