EpoxAcast™ Serie

Gießbare Epoxide werden für verschiedene industrielle Anwendungen verwendet. Sie sind einfach zu verwenden, enthalten keine VOCs und sind lösungsmittelfrei.

Verfügbar in EpoxAcast™ Serie

Product	Color	Flexural Strength	Flexural Modulus	Specific Volume	Specific Gravity	Shrinkage	Dielectric Strength	Heat Deflection Temperature	Volume Resistivity	Compressive Strength	Volume Resistance	Tensile Elongation	Tensile Modulus	Compressive Modulus	Mixed Viscosity	Mixed Viscosity With HT Hardener	Barcol Hardness	Ultimate Tensile Strength	Ultimate Tensile Strength With HT Hardener	Tensile Modulus With HT Hardener	Tensile Elongation With HT Hardener	Flexural Strength With HT Hardener	Flexural Modulus With HT Hardener	Compressive Strength With HT Hardener	Compressive Modulus With HT Hardener	Shrinkage With HT Hardener	Heat Deflection Temperature With HT Hardener	Dielectric Constant At 60 Hz	Dielectric Constant At 1 KHz	Color With HT Hardener	Storage Temperature	Shore D Hardness	Thermal Conductivity	Maximum Casting Volume	Maximum Heat Resistance	Mixed Viscosity (101, 102, 103 Hardener)	Mixed Viscosity (HT Hardener)	Specific Gravity (101, 102, 103 Hardener)	Specific Gravity (HT Hardener)	Specific Volume (101, 102, 103 Hardener)	Specific Volume (HT Hardener)	Ultimate Tensile Strength (101, 102, 103 Hardener)	Ultimate Tensile Strength (HT Hardener)	Tensile Modulus (101, 102, 103 Hardener)	Tensile Modulus (HT Hardener)	Tensile Elongation (101, 102, 103 Hardener)	Tensile Elongation (HT Hardener)	Compressive Strength (101, 102, 103 Hardener)	Compressive Strength (HT Hardener)	Compressive Modulus (101, 102, 103 Hardener)	Compressive Modulus (HT Hardener)	Shrinkage (101, 102, 103 Hardener)	Shrinkage (HT Hardener)	Heat Deflection Temperature (Room Temperature Cure)	Heat Deflection Temperature (Post Cured)	Cure Time	Specific Gravity	Specific Volume	Color	Tensile Strength	Tensile Modulus	Compressive Strength	Compressive Modulus	Flexural Strength	Shrinkage	Heat Deflection Temp	Tensile Elongation	Flexural Modulus	Mixed Viscocity	Mix Ratio By Weight	Pot Life	Shore D Hardness	Mixed Viscocity	Cure Time	Pot Life	Mix Ratio By Weight	Tensile Strength	Heat Deflection Temp	Refractive Index	Refractive Index	Ultimate Tensile	Ultimate Tensile
EpoxAcast™ 650	Off-White	5,890 PSI	710,000 PSI	18.22 cu. in./lb	1.52 g/cc	0.001 in/in	404 V/mil	129°F / 54°C	>3.59E+15 ohm cm	16,350 PSI	>5.42E+11 ohm	0.42%	1,503,000 PSI	142,600 PSI	7,000 CPS	5,000 CPS	93.000000	6,000 PSI	6,900 PSI	1,079,000 PSI	0.82%	10,850 PSI	775,000 PSI	15,980 PSI	134,400 PSI	0.007 in/in	187°F / 86°C	5.300000	5.080000	Black	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-
EpoxAcast™ 655	Grey	7,660 psi	1,403,000 psi	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	73°F/23°C	90	0.675 W/(m*K)	8,390 cm³	225°F/108°C	23,000 cps	12,000 cps	1.66 g/cc	1.64 g/cc	16.7 cu. in./lb	16.5 cu. in./lb	4810 psi	6,000 psi	2,040,000 psi	7,200,000 psi	0.54%	0.50%	12,500 psi	15,700 psi	125,500 psi	270,000 psi	0.0006 in./in.	0.001 in./in.	135°F/57°C	225°F/108°C	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-
EpoxAcast™ 670 HT	Beige	11,000 psi	254,000 psi	20.51 cu. in./lb.	1.15 g/cc	0.002 in. / in.	-	-	-	13,000 psi	-	0.65 %	332,000 psi	101,400 psi	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	90	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	<p>Twenty Four Hours Followed By Post Cure</p >	1.15 g/cc	20.51 cu. in./lb.	Beige	4,500 psi	332,000 psi	13,000 psi	101,400 psi	11,000 psi	0.002 in. / in.	350 °F	0.65 %	254,000 psi	6,000 cps	100A:16B	3 h.	90	6,000 cps	<p>Twenty Four Hours Followed By Post Cure</p >	3 h.	100A:16B	4,500 psi	350 °F	-	-	-	-
EpoxAcast™ 690	Clear	10,980 psi	410,000 psi	25 cu. in./lb.	1.10 g/cc	0.002 in. / in.	-	-	-	9,610 psi	-	1.8 %	572,000 psi	91,300 psi	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	80	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	24 h.	1.10 g/cc	25 cu. in./lb.	Clear	6,630 psi	572,000 psi	9,610 psi	91,300 psi	10,980 psi	0.002 in. / in.	115 °F	1.8 %	410,000 psi	280 cps	100A:30B	5 h.	80	280 cps	24 h.	5 h.	100A:30B	6,630 psi	115 °F	1.565 nm	1.565 nm	-	-
EpoxAcast™ 692 Deep Pour	Clear	6,780 psi	203,000 psi	25.7 cu. in./lb.	1.08 g/cc	0.007 in. / in.	-	-	-	5,777 psi	-	3.1 %	378,000 psi	82,000 psi	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	80	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	1.08 g/cc	25.7 cu. in./lb.	Clear	-	378,000 psi	5,777 psi	82,000 psi	6,780 psi	0.007 in. / in.	100 °F	3.1 %	203,000 psi	370 cps	100A:40B	12 h.	80	370 cps	-	12 h.	100A:40B	-	100 °F	1.5372 nm	1.5372 nm	4,585 psi	4,585 psi
EpoxAcast™ Hardener	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-	-

Warum bei FormX kaufen?

Wir lieben Material

Seit über dreißig Jahren suchen wir weltweit nach den hochwertigsten Materialien für Modellbau, Formenbau und Guss.
Inspirierend + Einzigartig

Von Silikonen und Harzen bis zu Jesmonite und Special-Effects-Materialien — ein sorgfältig kuratiertes Sortiment für Profis, Künstler und Macher.
Fachkundige Beratung

Unser Vertriebsteam ist bekannt für sein Wissen und Engagement und unterstützt Sie bei Formenbau, Guss, Bildhauerei und Prototyping.
Versand in ganz Europa

Wir versenden aus unseren Lagern in Amsterdam, Barcelona und Madrid an Kunden in ganz Europa, von Griechenland bis Norwegen.
Amsterdamer Original

FormX wurde in Amsterdam gegründet und wuchs von einer lokalen Kunstgießerei zu einem bedeutenden europäischen Lieferanten — mit festen Wurzeln in der Stadt.

FormX ist auf die Versorgung und den spezialisierten Handel mit 3D-Modelliermaterialien im weitesten Sinne des Wortes spezialisiert und verfügt über Lager und Showrooms in Amsterdam, Barcelona und Madrid.

Rechtliches

Webshop

Über

Gemeinschaft

Diese Website wurde entwickelt von Usecue B.V.
© 2026 FormX B.V.